Structural Elucidation of the Polymeric Condensed Tannins of <i>Acacia nilotica</i> Subspecies by C NMR, MALDI-TOF and TMA as Sources of Bioadhesives - Université de Pau et des Pays de l'Adour
Article Dans Une Revue Journal of Renewable Materials Année : 2024

Structural Elucidation of the Polymeric Condensed Tannins of Acacia nilotica Subspecies by C NMR, MALDI-TOF and TMA as Sources of Bioadhesives

Résumé

Tannin was extracted from different subspecies of Acacia nilotica, Acacia nilotica nilotica (Ann), Acacia nilotica tomentosa (Ant) and Acacia nilotica adansonii (Ana). The aim was to elucidate their structure and evaluate their reactivity as bioadhesives in the wood industry. The extracts were prepared by hot water extraction (90°C temperature). Their gel time with paraformaldehyde was used at first to compare their reactivity. The tannin contents and the percentage of total polyphenolic materials in different solutions of the extracts spray dried powder were determined by the hide powder method. Concentrated solutions (47%) were tested by both MALDI ToF, 13 CNMR. The thermomechanical analysis (TMA) was performed to evaluate their modulus of elasticity (MOE) at different pHs. The gel times of all the three tannin extracts showed that their reactivity and it was comparable to other known procyanidin/prodelphinidin tannin extract types. Ana, Ann and Ant showed highest percent of total polyphenolic materials at 70%, 64%, and 57%, respectively. The 13CNMR spectra showed that the three subspecies of condensed tannins were mainly constituted of procyanidins (PC) and prodelphinidins (PD) in slightly different ratios. Ann (56.5% PC and 43.4% PD), Ant (57%PC and 43% PD) and Ana (58% PC and 42% PD). MALDI-TOF spectra showed the presence of flavonoid monomers, and oligomers some of which linked to short carbohydrates monomers or dimers. TMA revealed that the three types of tannins had high MOE at their initial pH (5).

Fichier principal
Vignette du fichier
TSP_JRM_51619.pdf (3.88 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-04691641 , version 1 (09-09-2024)

Identifiants

Citer

Zeinab Osman, Antonio Pizzi, Bertrand Charrier. Structural Elucidation of the Polymeric Condensed Tannins of Acacia nilotica Subspecies by C NMR, MALDI-TOF and TMA as Sources of Bioadhesives. Journal of Renewable Materials, 2024, 12 (7), pp.1291 - 1310. ⟨10.32604/jrm.2024.051619⟩. ⟨hal-04691641⟩
67 Consultations
15 Téléchargements

Altmetric

Partager

More